期刊
POLYMER
卷 48, 期 11, 页码 3286-3293出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymer.2007.03.070
关键词
polymer nanocomposites; deformation behaviour; simultaneous SAXS and WAXS
Relationships between the macroscopic deformation behaviour and microstructure of a pure (PBT-b-PTMO) block copolymer and a polymer nanocomposite (PBT-b-PTMO + 0.2 wt% SWCNT) were investigated by simultaneous small- and wide-angle X-ray scattering (SAXS and WAXS) during tensile deformation using synchrotron radiation. The Young's modulus was found to be 15% higher for the nanocomposite than for the pure block copolymer as well as the yield strength, while the elongation-to-break was less than a half. This different behaviour can be explained by taking into account the different structural features revealed by SAXS and WAXS and thus considering that SWCNT act as anchors in the nanocomposite, sharing the applied stress with the PBT crystals and partially preventing the flexible, non-crystallisable PTMO chains to elongate. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据