JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 313, 期 1, 页码 62-68出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmmm.2006.12.004
关键词
monolayer deposition; electrospray; FePt nanoparticle; phase transformation
The deposition monolayers of L1(0) FePt nanoparticles via an electrospraying method and the magnetic properties of the deposited film were studied. FePt nanoparticles in a size of around 2.5 nm in diameter, prepared by a liquid process, were used as a precursor. The size of the deposited particles can be controlled up to 35 nm by controlling the sprayed droplet size that is formed by adjusting the precursor concentration and the precursor flow rate. The droplets were heated in a tubular furnace at a temperature of up to 900 degrees C to remove all organic compounds and to transform the FePt particles from disordered face centered cubic to an ordered FCT phase. Finally, the particles were deposited in the form of a monolayer film on a silicon substrate by electrostatic force and characterized by scanning electron microscopy. The monolayer of particles was obtained by the high charge on particles obtained during the electrospraying process. The magnetic properties of the monolayer were investigated by magneto-optic Kerr effect measurements. Coercivity up to 650 Oe for a film consisting of 35 nm L1(0) FePt nanoparticles was observed after heat treatment at a temperature of 800 degrees C. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据