ENGINEERING FAILURE ANALYSIS
卷 14, 期 4, 页码 673-685出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.engfailanal.2006.02.016
关键词
fatigue life; discontinuity; aluminum alloys; nucleation; cladding; anodizing
The current methods of fatigue life estimation do not model the interaction of stress with microstructural discontinuities. An experimental study of fatigue crack nucleation in 7075-T6 and 7079-T6 aluminum alloy sheet was performed to obtain more information on the role of discontinuities in the microstructure and to determine the relative contributions of each type of discontinuity. Some specimens were machined from recently manufactured material without any coating (cladding or anodizing). Some were fabricated from old clad-anodized material from an aircraft fuselage and old anodized material from a stock of unused wing panels. In the uncoated materials, large constituent particles and the surface roughness were found to be important factors in fatigue crack nucleation. In the coated materials, discontinuities related to the cladding and anodizing appeared to be the controlling factors in crack nucleation and particles did not play any role. The coated specimens showed a low scatter and a relatively low fatigue life. Multiple nucleation sites were observed in the coated materials. (c) 2006 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据