Swelling and cation exchange capacity relationship for the samples obtained from a bentonite by acid activations and heat treatments

期刊

APPLIED CLAY SCIENCE
卷 37, 期 1-2, 页码 74-80

出版社

ELSEVIER SCIENCE BV
DOI: 10.1016/j.clay.2006.12.004

关键词

acid activation; bentonite; cation exchange capacity; heat treatment; swelling

向作者/读者索取更多资源

To investigate the effect of heating and acid activation on the cation exchange capacity (CEC) and swelling (SWE), a calcium bentonite (CaB) was used. The calcium bentonite (CaB) from the Kutahya (Turkey) region contains approximately 65% and 30% by mass calcium reach smectite (CaS) and opal-CT (OCT), respectively. The rest amount is illite (1) and other impurities. The 13 samples were heated at different temperatures between 100 and 1300 degrees C for 2 h. Furthermore, the sample was activated with H2SO4 having various dosages ranging between 0 and 70% by mass in the dry bentonite-acid mixture, by heating the aqueous suspensions at 97 degrees C for 6 h. The CEC and total SWE (crystalline and osmotic) were measured by the standard methylene blue (MB) method and as gel volume in definite amount water, respectively. The CEC and SWE decrease by the heating depending on the collapse of the 2:1 layers of the CaS. While the SWE decreases approximately linearly by increasing of the temperature, the CEC decreases faster after 600 degrees C and reaches to zero at 900 degrees C. While the CEC increases almost linearly with the H2SO4 dosage by the activation, the SWE decreases up to 20% and then does not change. In general, the SWE increases with CEC. (C) 2006 Elsevier B.V. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据