hot extrusion; Al/SiC composites; extrusion temperature; porosity; microstructure; particle cracking
The effect of extrusion temperature on the microstructure and porosity of Al A356-10vo1.% SiC composites was investigated. Composites containing three different particle sizes of 38, 62 and 82 mu m fabricated by compocasting (SL) method were extruded at three different temperatures of 450, 500, and 550 degrees C using an extrusion ratio of 18:1. The extruded composites exhibited reduced porosity as well as a more uniform particle distribution when compared with the as-cast samples. Image analysis showed that the SiC particles were refined by the extrusion process and that the extent of the refinement decreased with the extrusion temperature. These results indicate the extrusion-induced particle fracture when particle-reinforced metal matrix composites (MMCs) are extruded at a relatively low temperature. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据