期刊
JOURNAL OF PHYSICAL CHEMISTRY C
卷 111, 期 23, 页码 8389-8396出版社
AMER CHEMICAL SOC
DOI: 10.1021/jp071223f
关键词
-
Hydrogenation-dehydrogenation properties in a Mg-added LiH-LiNH2 hydrogen storage system were examined by using a newly developed gas chromatography technique with hydrogen pulse detection as 2LiNH(2) + Mg(surface) <--> Mg(LiNH2)(2) <--> Mg(LiNH)(2) + H-2, Mg(LiNH)(2) + 2LiH <--> Mg(Li2N)(2) + 2H(2) (6.96 mass %). The improved performance of hydrogen storage was found by preparing a Mg additive instead of MgH2 or Mg(NH2)(2). A high plateau pressure of > 0.1 MPa at 175 degrees C, which was obtained from PCT measurements, yielded lower dehydrogenation temperatures of 169 and 193 degrees C in Mg/LiH/LiNH2 = 0.5/1/1 and 0.25/1/1 (DTA results), respectively. The reversibility was confirmed from the results of redehydrogenation after rehydrogenation at a pressure of 1 MPa in the temperature range 150-250 degrees C over 1-3 h, but dehydrogenation properties showed little difference. It was concluded that the change in the dehydrogenation kinetics may be caused by the difference in temperature between hydrogenation and dehydrogenation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据