Yb3+; Yb2+; Ni -and Fe- impurities; YAG; YbAG; cooperative energy transfer; quantum efficiency; photoconductivity; ENDOR
类别
In this work, the growing process of Yb-doped YAG crystals is modified to achieve stoichiometric YbAG samples with a minimum quenching of the Yb3+-fluorescence. The best samples were grown by the Czochralski technique from rhenium-crucibles under reducing atmosphere (H-2 + N-2). The as-grown YbAG crystals are of light blue color due to Yb2+-centers. The fluorescence lifetime of Yb3+ after annealing the YbAG crystals under oxidizing atmosphere is 862 +/- 15 mu s. The non-annealed samples show strong quenching of the Yb3+-fluorescence with a lifetime of only a few tens of microseconds depending on the actual growth conditions. This strong quenching is partially attributed to the Yb2+-centers giving rise to a cooperative energy transfer process among two excited Yb3+-ions and one nonexcited Yb2+-ion. Typical quenching centers in Yb:YAG crystals grown from Ir-crucibles are Fe- and Ni-impurities. Another effective quenching center in non-annealed crystals is a complex center consisting of a Si2+-ion and a charge compensating oxygen vacancy with one trapped electron (F+ color center). This type of center was identified by ESR- and ENDOR-measurements. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据