期刊
MATERIALS TRANSACTIONS
卷 48, 期 7, 页码 1680-1683出版社
JAPAN INST METALS
DOI: 10.2320/matertrans.MJ200748
关键词
metallic glass; rapid solidification; thermal properties; rare earth alloys; glass-forming ability
In this paper, a pseudo-ternary (La0.5Ce0.5)(65)Al10Co25 alloy with high glass-forming ability (GFA), identified by the formation of glassy rods up to 12 rum in diameter by copper mold casting. was reported. Furthermore, according to the viewpoint that similar element coexistence can be beneficial to improve the GFA, Cu was chosen as the similar element to substitute for solute Co in (La0.5Ce0.5)(65)Al-10(Co1-xCux)(25) alloys (0 <= x <= 1). The influence of this substitution on thermal stability, melting and solidification behaviors of these metallic glasses was evaluated. The optimized (La0.5Ce0.5)(65)Al-10(Co0.6Cu0.4)(25) alloy with high reduced glass transition temperature (0.66) and the large nominal supercooled degree (114 K) can form the fully glassy rods up to at least 25 mm in diameter by tilt-pour casting.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据