copper; composite; thermo-mechanical processing; Vickers hardness; electrical conductivity
Thermo-mechanical treatments with stepped annealing were investigated to improve the strength and conductivity of Cu-1 lFe-6Ag in situ composite. Changes in microstructure, Vickers hardness and conductivity of the heat-treated composite were studied. The results show that stepped annealing at a certain draw ratio produce better combination of strength and conductivity. After three stepped annealing at 77 = 4.1, 5.5 and 6.9, Cu-1 lFe-6Ag obtain strength/conductivity combination of 1140 MPa/68% IACS at eta = 7.6 and 1260 MPa/63.8% IACS at eta = 8.3, which are the best combination reported for Cu-Fe system to date. However, that of the same processed Cu-12Fe is only 962 MPa/62% IACS at eta = 7.6. The two composites exhibit different responses to the treatment due to the role of Ag: strengthening the composite in the form of precipitations and fibers and accelerating precipitation kinetics of Fe from the matrix. (C) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据