MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 462, 期 1-2, 页码 259-263出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2006.04.154
关键词
warm deformation; ferrite; dynamic softening; continuous dynamic recrystallization; C-Mn steel
The evolution of dynamic ferrite softening in a plain-carbon steel was investigated by torsion tests during warm deformation at 810 degrees C, in the two-phase (ferrite + austenite) region, and strain rate of 0.1 s(-1) with different strains up to 50. The warm flow behaviour and ferrite microstructural parameters, such as grain size, misorientation angle across ferrite/ferrite boundaries, and the fraction of high-angle and low-angle grain/subgrain boundaries were quantified using electron back scatter diffraction. The results show that with increasing strain up to similar to 2, the ferrite grain size and fraction of high-angle boundaries rapidly decrease and the fraction of low-angle boundaries increases. However, these parameters remain approximately unchanged with increasing strain from similar to 2 to 50. The dynamic softening mechanism observed during large strain ferritic deformation is explained by dynamic recovery and continuous dynamic recrystallization. (C) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据