期刊
EUROPEAN POLYMER JOURNAL
卷 43, 期 8, 页码 3621-3628出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.eurpolymj.2007.06.002
关键词
organic inorganic hybrid materials; sol-gel process; quaternary ammonium salt; antibacterial activity; polyethylene
Organic-inorganic hybrid coatings containing quaternary ammonium salts (QAS) bonded to the organic-inorganic network were prepared from tetraethoxysilane and triethoxysilane terminated poly(ethylene glycol)-block-poly(ethylene) using a sol-gel process. They were applied as a thin layer (0.6-1 mu m) to PE films and the antibacterial activity of the coated films was tested against both Gram-negative (Escherichia coli ATCC 25922) and Gram-positive (Staphylococcus aureus ATCC 6538) bacteria. Measurements at different contact times showed a rapid decrease of the viable count for both the tested strains. In particular, after 48 h of contact, a decrease of 96.4% and 99.1% of E coli and S. aureus, respectively, was observed. The permanence of the antibacterial activity of the coated films was demonstrated through repeated washings and prolonged immersion in physiological saline solutions at 37 degrees C. Indeed, due to the removal of QAS moieties by the nucleophilic attack of water, the antibacterial activity after 24 h was strongly reduced when measured on samples submitted to several washings. However, a quite good antibacterial activity was observed even on the same samples after 96 h, probably due to a spontaneous partial restoring of the QAS on the surface. Very good transparency, quite good adhesion and high wettability are further features of these hybrid coatings. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据