POLYMER DEGRADATION AND STABILITY
卷 92, 期 8, 页码 1446-1454出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2007.05.010
关键词
polyurethane; butadiene; FTIR; microspectroscopy; oxidation
Hydroxy-terminated polybutadiene/isophorone diisocyanate (HTPB/IPDI) polyurethane rubber which was aged in air at elevated temperatures has been studied by infrared microspectroscopy. Spectra were collected in transmission mode on microtomed samples. Analysis of sets of spectra taken across the sectioned material showed that most of the degradation occurred in the polybutadiene part of the polymer and that the urethane linkage was essentially unchanged. The trans isomer of the polybutadiene appears to be preferentially degraded compared with the vinyl isomer. The IR technique does not provide significant information about the cis isomer. The IR spectra indicated that likely degradation products included acids, esters, alcohols, and small amounts of other products containing a carbonyl functional group. Band area ratios, supported by a principal components analysis, were used to derive degradation profiles for the material. These profiles were steep-sided indicating an oxygen diffusion limited process. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据