期刊
MATERIALS AND STRUCTURES
卷 40, 期 7, 页码 679-691出版社
SPRINGER
DOI: 10.1617/s11527-006-9181-1
关键词
microfibers; toughening mechanisms; cement-based materials; crack growth resistance behavior; multiple cracking; intergrinding of fibers
Performance enhancement due to microfibers is well known. However, fracture processes that lead to strain hardening behavior in microfiber reinforced composites are not well understood. Crack growth resistance behavior of mortar reinforced with steel microfibers and polypropylene microfibers was investigated in-situ during load application. The polypropylene fibers were inter-ground in the cement mill to enhance the fiber/matrix interfacial frictional stress. A more homogeneous fiber distribution was observed in the inter-ground polypropylene composites compared to the steel microfiber reinforced composites. In steel microfiber reinforced composites the dominant toughening mechanisms were multiple microcracking and successive debonding along the fiber/matrix interface. Fiber pullout, the dominant mechanism in conventional macrofiber reinforced composites was rarely observed. In-situ observation of crack/fiber interaction in the inter-ground polymer fibers also revealed multiple microcracking along the length of the fibers followed by fiber pullout.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据