diacylhydrazides; dianhydrides; poly(amideimide)s; alkoxy side chains; thermal stability
A series of aromatic diacylhydrazides containing pendent flexible alkoxy chains, viz., 5-butyloxyisophthalicacid dihydrazide, 5-octyloxyisophthalicacid dihydrazide, 5-dodecyloxyisophthalicacid dihydrazide and 5-hexadecyloxyisophthalicacid dihydrazide were synthesized by the hydrazinolysis reaction of the corresponding aromatic esters with hydrazine hydrate. Diacylhydrazides were each polycondensed with aromatic dianhydrides, viz., 4,4'-oxydiphthalic anhydride (ODPA), 3,3',4,4'-biphenyltetracarboxylic dianhydride (BPDA) and pyromellitic dianhydride (PMDA) to obtain new poly(amideimide)s. Poly(amideimide)s had inherent viscosity in the range 0.55-0.88 dL/g in N,N-dimethylacetamide (DMAc) at 30 +/- 0.1 degrees C. Poly(amideimide)s were found to be soluble in DMAc, N,N-dimethylformamide (DMF), 1-methyl-2-pyrrolidinone (NMP) and pyridine and could be cast into tough, flexible and transparent films from a solution in DMAc. X-ray diffractograms revealed that poly(amideimide)s with longer alkoxy chains had layered structures. Glass transition temperature of poly(amideimide)s containing pendent flexible alkoxy chains were in the range 215-245 degrees C. Temperature at 10% weight loss was in the range 380-410 degrees C in nitrogen atmosphere indicating good thermal stability of poly(amideimide)s. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据