MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 464, 期 1-2, 页码 170-176出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2007.01.132
关键词
WC-Co cladding; laser cladding; laser material deposition; pulsed solid state laser
Laser cladding is an advanced material processing technology that has potential to deposit various materials locally on highly non-planar and complex surfaces. It can be used to refurbish or improve corrosion, wear and other surface related properties of components. The laser cladding of WC-Co using continuous wave (CW) laser has been tried and problems, like-cracks, porosity, poor bonding, partial melting of WC particles in the Co matrix, etc., have been observed. To resolve these issues, the successful laser cladding with alternate binder materials, like-Ni, Fe, Co-Cr, Ni-B-Si, etc., have been reported. In the presentstudy, a pulsed Nd:YAG laser was used to deposit multi-layer overlapped cladding on low carbon steel substrate using dynamic powder blowing technique. Thus, produced laser cladding samples were subjected to various mechanical tests and metallurgical analyses. The results showed that fully dense and crack free clad surfaces of WC-Co with an excellent metallurgical bonding and low dilution were deposited. No melting of WC particles in the Co matrix was observed during the microscopy. The average microhardness at the clad surface was about 1350 HV, while that at substrate was 200 HV. The observed adhesion strength of the WC-Co cladding to the substrate was about 60 MPa. (c) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据