期刊
JOURNAL OF CRYSTAL GROWTH
卷 307, 期 1, 页码 229-234出版社
ELSEVIER
DOI: 10.1016/j.jcrysgro.2007.06.018
关键词
PL; annealing; MOCVD; GaNAs
In this study, rapid thermal annealing (RTA) of GaNAs epilayers at different temperatures was performed and their photoluminescence (PL) performance with different annealing temperatures was investigated. Two emission peaks have been observed from the GaNAs epilayers. The first peak (higher photon energy) is related to the energy band-gap transition emission of the alloy, while the second peak (with lower photon energy) is related to defect trap emission. It is seen that the PL intensity of the samples' energy band-gap transition improved with annealing and at the same time the emission peaks red shifted. However, the defect-related emission of the sample is suppressed by the RTA annealing. The optimum annealing temperature was defined as the highest PL integrated intensity of the first peak of the annealed GaNAs samples. It is found that the optimum annealing temperature is dependent on nitrogen concentration of GaNAs epilayer, it decreases with higher N composition sample. With an SiO2 cap layer on the GaNAs samples, PL intensity of the band-gap emission of the annealed samples was further improved. An SiO2 cap layer is more effective for improving the PL emission intensity of samples with a higher N content than those with a lower N content. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据