POLYMER DEGRADATION AND STABILITY
卷 92, 期 9, 页码 1645-1649出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2007.06.013
关键词
plasma treatment; poly(ethylene); surface topography; chemical structure; ablation; water etching
Ablation and water etching of high density polyethylene (PE) exposed to Ar plasma for 240 s at 8.3 W power were studied. Gravimetry was used to determine the ablated and etched layer thicknesses. The surface topography and roughness were observed via AFM. The chemical composition and structure of modified surface layer were studied by FTIR, XPS, RBS, and EPR techniques. It was found that under the experimental conditions ca. 30 nm thick layer is ablated, the surface topography changes dramatically and surface roughness increases. The cleavage of macromolecular chains is proved by the presence of surface free radicals. Oxygen containing groups known to enhance surface solubility are detected. Under present laboratory conditions ca. 20 urn thick surface layer is dissolved during 24 h. After water dissolution of the surface, the roughness increases. (C) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据