JOURNAL OF COLLOID AND INTERFACE SCIENCE
卷 316, 期 1, 页码 85-91出版社
ACADEMIC PRESS INC ELSEVIER SCIENCE
DOI: 10.1016/j.jcis.2007.07.037
关键词
mesoporous TiO2; photocatalytic activity; calcination temperature; pore size; porous structure
资金
- National Research Foundation of Korea [R11-1999-064-09003-0, 과C6A2003] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
Mesoporous TiO2 materials with various pore-size distributions were synthesized by using diblock copolymers via a sol-gel process in aqueous solution. The properties of these materials were characterized by FE-SEM, HR-TEM, XRD, DRS, BET, and BJH analysis. All particles have spherical morphology with a diameter range of 1-3 mu m. The mesoporous TiO2 materials calcined at 400 degrees C were found to have different specific surface areas-186, 2 10, and 192 m(2) g(-1) -and average pore sizes depending on the type of diblock copolymer-5.1, 6.1, and 6.4 nm-and their crystallite sizes were found to be 8.1, 8.3, and 8.8 nm. The photocatalytic activity of each sample was investigated by measuring the photodecomposition of methylene blue (MB), and the small crystallite size, large surface area, and small pore size were found to exhibit better photocatalytic activities. In addition, the photocatalytic activities of all the mesoporous TiO2 materials were found to be better than that of commercial TiO2. (C) 2007 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据