期刊
EUROPEAN POLYMER JOURNAL
卷 43, 期 12, 页码 5047-5054出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.eurpolymj.2007.08.016
关键词
poly(amide-imide)s; sulphone and bulky pendant groups; direct polycondensation; thermally stable polymers
A novel diimide-diacid (DIDA) monomer, 4-{4-[(4-methyl phenyl) sulphonyl]}-1,3-bis-trimellitoimido benzene containing sulphone and bulky pendant groups was successfully synthesized and used to synthesize a series of wholly aromatic poly(amide-imide)s (PAIs) by direct polycondensation method. The direct polycondensation of newly synthesized DIDA with different diamines was carried Out via Yamazaki's phosphorylation method using triphenyl phosphite and pyridine system. The resulting poly(amide-imide)s were obtained in quantitative yields with inherent viscosities 0.36-0.47 dl/g in DMAc at 30 +/- 0.1 degrees C. The poly(amide-imide)s were amorphous and were readily soluble in various solvents such as N-methyl-2-pyrrolidinone (NMP), NN-dimethylacetamide (DMAc), N,N-dimethylformamide (DMF), dimethylsulfoxide (DMSO), and pyridine. Tough and flexible films were obtained by casting their DMAc solution. According to thermogravimetric analysis, the polymers were fairly stable up to temperature around 396 degrees C, and 10% weight losses in the temperature range of 476-511 degrees C that showed good thermal stabilities of these polymers. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据