lithium manganese oxide; Li0.44MnO2; tunnel structure; ion exchange; lithium insertion; electrochemical property
The specific capacity of Li0.44Mn1-yTiyO2 (O<0.22) positive electrode materials has been improved by an additional lithium-insertion treatment in molten LiNO3-LiOH salt at a low temperature. High-purity specimens of the lithium-inserted Li0.44+xMn1-yTiyO2 have been successfully prepared. We have conducted a systematic experimental study of the structural and electrochemical properties of these compounds. The inserted lithium content, x, in Li0.44+xMn1-yTiyO2 increases together with the substituted Ti content, y. The initial charge capacity increases from 130 mAh g(-1) (y = 0) to 145 mAh g(-1) (y = 0.22) for the Li0.44+xMn1-yTiyO2 compounds. The maximum discharge capacity that has been achieved is 180 mAh g(-1) in the case of Li0.72Mn0.78Ti0.22O2 between 2.5 and 4.8 V with a fixed current density of 30 mA g(-1) (C/6) at 30 degrees C. The discharge capacity at the 4 V plateau region (about 100 mAh g(-1)) in the lithium-inserted Li0.55MnO2 has been improved to twice that in as-prepared Li0.44MnO2 (about 50 mAh g(-1)). The structural differences between Li0.44MnO2 and Li0.55MnO2 are discussed based on XRD Rietveld analysis results. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据