JOURNAL OF APPLIED POLYMER SCIENCE
卷 107, 期 2, 页码 1207-1214出版社
JOHN WILEY & SONS INC
DOI: 10.1002/app.27188
关键词
polyurethane/acrylic hybrids; FTIR; H-1-NMR spectrum; thermal properties
Polyurethane (PU) polymer was synthesized following a prepolymer mixing process, by polyaddition of isophorone diisocyanate (IPDI), poly(propylene glycol) (PPG), 2-hydroxyethyl methacrylate (HEMA), and 2,2-bis(hydroxymethyl)propionic acid (DMPA). The PU anionomer having 2-ethoxymethacrylate terminal groups was dispersed in water by prior neutralization of carboxylic acid groups of DMPA with triethylamine (TEA), chain extended with hydrazine (HZM) in water and a dispersion polymerization with methyl methacrylate/n-butyl acrylate/acrylic acid mixture was performed. The above polymerization reactions lead to the formation of PU/acrylic hybrids having a chemical bond between PU and acrylic moieties. Acrylic content was varied from 0 to 50 wt % and samples were purified to eliminate oligomers and impurities before characterization. The FTIR and H-1-NMR spectra of these purified hybrid samples were obtained and bands and peaks assignments were discussed. Thermal properties (DSC and TGA) were also discussed. Breaking hydrogen bonds is the main reason for changes in properties with increasing acrylic content. Particle size data of dispersions is also presented and discussed. (C) 2007 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据