\ Size effect in the fatigue behavior of Friction Stir Welded plates

期刊

INTERNATIONAL JOURNAL OF FATIGUE
卷 80, 期 -, 页码 238-245

出版社

ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2015.06.010

关键词

Size effect; Fatigue life; Equivalent Initial Flaw Size; Friction Stir Welding

向作者/读者索取更多资源

Comparative fatigue tests were carried out on Friction Stir Welded specimens of a 2195-T8 aluminum-lithium alloy that differed significantly in width. The width of the larger specimens was over thirteen times greater than that of the small specimens. Fatigue results showed a clear size effect, i.e. fatigue life of large specimens was about 40% of the corresponding value of small specimens. The Equivalent Initial Flaw Size methodology was adopted to correlate the two sets of results. Fatigue crack initiation life was disregarded with respect to crack propagation life, and fatigue life was evaluated only as propagation of a small pre-existing defect. Following this methodology, test results of small specimens were used to evaluate the initial equivalent flaw contained in each specimen. It was assumed that this data followed a normal distribution. The equivalent initial flaw in larger specimens was evaluated by simple geometrical considerations. A very good assessment of mean fatigue life and scatter in the fatigue results of large specimens was obtained by simulating the propagation of these defects. Calculations were carried out by taking also welding residual stresses into account, but the results demonstrated that this effect was not significant. (C) 2015 Elsevier Ltd. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据