JOURNAL OF THE CERAMIC SOCIETY OF JAPAN
卷 117, 期 1362, 页码 198-202出版社
CERAMIC SOC JAPAN-NIPPON SERAMIKKUSU KYOKAI
DOI: 10.2109/jcersj2.117.198
关键词
Mesoporous silica; Spray-drying process; Aerosol-assisted process; Surfactant assemblies
资金
- The Murata Science Foundation [19850031]
A spray-drying process was applied to the mass-production of mesoporous silica particles. The applied nozzle pressure and amount of solvent in the precursor solution were varied to control the average particle size. The particle-size distribution showed a bell curve with a normal distribution. As the nozzle pressure was increased from 0.05 to 0.20 MPa, the average particle size was decreased proportionally. In addition, as the surfactant concentrations in the precursor solutions were decreased, the average particle size was decreased. Based on the results of low-angle X-ray diffraction measurements, N-2 adsorption measurements, and TEM observations, it was proven that well-ordered mesoporous structures were formed inside the particles. It is proved that the spray-drying conditions do not affect the mesoporous structures but do affect the average particle size. (C) 2009 The Ceramic society of Japan. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据