INTERNATIONAL ENDODONTIC JOURNAL
卷 49, 期 2, 页码 184-188出版社
WILEY
DOI: 10.1111/iej.12433
关键词
biodentine; bond strength; intracanal medicaments; ProRoot MTA
Aim To evaluate the effect of prior application of several intracanal medicaments on the push-out bond strength of ProRoot MTA and Biodentine. Methodology Sixty freshly extracted maxillary anterior teeth were sectioned below the cementoenamel junction, and the root canals instrumented using rotary files. Thereafter, a parallel post drill was used to obtain a standardized root canal dimension. The roots were randomly assigned into one of the following groups with respect to the intracanal medicament applied: group 1: calcium hydroxide (CH) powder (Merck, Darmstadt, Germany) mixed with distilled water; group 2: a mixture of metronidazole, ciprofloxacin and minocycline (triple antibiotic paste); group 3: a combination of amoxicillin and clavulanic acid (Augmentin; Champs Pharmacy, San Antonio, TX, USA); group 4: an antibiotic-corticoid compound paste (Ledermix; Riemser, Greifswald, Germany); and group 5: no medicament (control). Following removal of medicaments with instrumentation and irrigation, the roots were cut into 1-mm-thick parallel transverse sections in a coronal-to-apical direction (5 slices/tooth). Thereafter, the specimens were divided into two subgroups according to the calcium silicate cement applied (n=30/group): (i) ProRoot MTA (Dentsply Tulsa Dental, Tulsa, OK, USA) and (ii) Biodentine (Septodont, Saint-Maur-des-Fosses, France). A push-out test was performed, and the data were analysed statistically using two-way anova and Tukey's post hoc test. Results Regardless of the type of intracanal medicament used, Biodentine had significantly higher bond strength than MTA (P<0.05). The highest push-out bond strength results were obtained in CH-treated dentine. Compared with other medicaments, this value was only significantly higher than that of Ledermix (P<0.05). In both the MTA and Biodentine groups, pairwise comparisons between other medicaments showed similar debonding values (P>0.05). Conclusions Biodentine had a higher bond strength to root canal dentine than ProRoot MTA. Prior CH in distilled water intracanal placement increased the dislodgment resistance of both calcium silicate cements.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据