期刊
ACTA MATERIALIA
卷 73, 期 -, 页码 167-176出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2014.04.004
关键词
Cu bicrystal; Twin boundary; Slip band; Fatigue crack; Molecular statics
资金
- National Natural Science Foundation of China (NSFC) [50890173, 51171194, 51331007, 11172264]
- National Basic Research Program of China [2010CB631006]
A Cu bicrystal with a twin boundary (TB) inclined at 45 degrees to the loading direction and its component monocrystal were specially designed to reveal their fatigue cracking mechanisms. Experimental results show that slip bands (SBs) parallel to the TB plane operated easily in both component grains and concentrated at the TB, while the SBs distributed more homogeneously in the monocrystal. It was revealed by atomistic modeling simulations and anisotropic elasticity theory that the screw dislocations transmitted to the TB could dissociate into two far-separated partial dislocations. Therefore, these dislocations would be confined in the TB with a high difficulty of cross-slip, leading to strain localization near the TB. With cyclic deformation, the fatigue crack nucleated along the TB preferentially in the bicrystal with fewer cycles than that for the SB crack in the monocrystal. Besides, unlike the impingement fatigue crack along high-angle grain boundaries with dislocation impingement, the shear fatigue crack initiates along the TB devoid of dislocation pile-ups. The existence of the TB inclined at 45 degrees to the loading direction induces strain localization and early intergranular fatigue cracking in the Cu bicrystal. These results could not only expand our knowledge of fatigue cracking mechanisms by clarifying how the boundary behaves without the piling up of dislocations, but also provide important implications for future interfacial optimization of materials. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据