Evolution of voids during ductile crack propagation in an aluminium alloy sheet toughness test studied by synchrotron radiation computed tomography

期刊

ACTA MATERIALIA
卷 56, 期 8, 页码 1671-1679

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2007.12.019

关键词

aluminium alloys; ductile fracture; synchrotron radiation computed tomography; anisotropy; non-spherical voids

向作者/读者索取更多资源

The anisotropy of fracture toughness in AA2139 (Al-Cu-Mg) alloy sheet has been investigated via synchrotron radiation computed tomography of arrested cracks in Kahn tear test pieces for different loading cases. The three-dimensional distribution and morphology of pores and defects in the as-received state are seen to be anisotropic, with chains of voids and void elongation in the L (longitudinal) direction. For toughness testing in L-T orientation (T is long transverse), voids ahead of the crack grow and link in the L direction. In T-L tests, voids ahead of the crack tip also grow in the loading direction, although a high degree of alignment is retained in the L direction. The present work provides quantitative microstructural data that can be used as input for and validation of recent idealized model formulations, and it is shown that the measured void dimensions and evolution are consistent with measured toughness anisotropy. (c) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据