期刊
ACTA CHIMICA SINICA
卷 70, 期 1, 页码 15-20出版社
SCIENCE PRESS
DOI: 10.6023/A1105275
关键词
lithium-ion battery; anode material; TiO2@MWNTs nanocomposites; solvothermal
资金
- National Natural Science Foundation of China [20873064, 21173120]
- Specialized Research Fund for the Doctoral Program of Higher Education of China [20060287026]
The TiO2@MWNTs nanocomposites have been prepared by a simple one-step solvothermal method using low-cost TiOSO4 as the raw material in the presence of MWNTs. X-ray diffraction (XRD), scan electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen adsorption-desorption and thermogravimetric-differential scanning calorimeter (TG-DSC) analysis were performed to characterize the structures and morphologies of the TiO2@MWNTs composites. Their lithium storage properties were investigated with galvanostatic charge/discharge measurements when the composites was used as anode materials for lithium-ion batteries (LIBs). The nitrogen adsorption-desorption curve and pore size distribution verified that the TiO2@MWNTs nanocomposites had rich hierarchical pores and large specific surface area. Compared with pristine TiO2, these TiO2@MWNTs nanocomposites exhibited much higher rate capability and even better capacity retention. The reversible capacity of the nanocomposites electrode is up to 200 mAh.g(-1) and remain at 182 mAh.g(-1) at 1 C after 100 cycles. The reversible capacity is about 100 mAh.g(-1) even at the high rate of 10 C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据