Photopolymerization of cell-encapsulating hydrogels: Crosslinking efficiency versus cytotoxicity

Cell-encapsulating hydrogels used in regenerative medicine are designed to undergo a rapid liquid-to-solid phase transition in the presence of cells and tissues so as to maximize crosslinking and minimize cell toxicity. Light-activated free-radical crosslinking (photopolymerization) is of particular interest in this regard because it can provide rapid reaction rates that result in uniform hydrogel properties with excellent temporal and spatial control features. Among the many initiator systems available for photopolymerization, only a few have been identified as suitable for cell-based hydrogel formation owing to their water solubility, crosslinking properties and non-toxic reaction conditions. In this study, three long-wave ultraviolet (UV) light-activtied photoinitiators (PIs) were comparatively tested in terms of cytotoxicity, crosslinking efficiency and crosslinking kinetics of cell-encapsulating hydrogels. The hydrogels were photopolymerized from poly(ethylene glycol) (PEG) diacrylate or PEG-fibrinogen precursors using Irgacure (R) PIs 12959,1184 and 1651, as well as with a chemical initiator/accelerator (APS/TEMED). The study specifically evaluated the PI type, PI concentration and UV light intensity, and how these affected the mechanical properties of the hydrogel (i.e. maximum storage modulus), the crosslinking reaction times and the reaction's cytotoxicity to encapsulated cells. Only two initiators (12959 and 1184) were identified as being suitable for achieving both high cell viability and efficient crosslinking of the cell-encapsulating hydrogels during the photopolymerization reaction. Optimization of PI concentration or irradiation intensity was particularly important for achieving maximum mechanical properties; a sub-optimal choice of PI concentration or irradiation intensity resulted in a substantial reduction in hydrogel modulus. Cytocompatibility may be compromised by unnecessarily prolonging exposure to cytotoxic free radicals or inadvertently enhancing the instantaneous dose of radicals in solution, both of which are dependent on the PI type/concentration and irradiation intensity. In the absence of a radical initiator, the short exposures to long-wave UV light irradiation (up to 5 min, 20 mW cm(-2), 365 nm) did not prove to be cytotoxic to cells. Therefore, it is important to understand the relationship between PIs, light irradiation conditions and crosslinking when attempting to identify a suitable hydrogel formation process for cell encapsulating hydrogels. (C) 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.