Apatite formation on alkaline-treated dense TiO2 coatings deposited using the solution precursor plasma spray process

A dense titania (TiO2) coating was deposited from an ethanol-based solution containing titanium isopropoxide using the solution precursor plasma spray (SPPS) process. XRD and Raman spectrum analyses confirmed that the coating is exclusively composed of rutile TiO2. SEM micrographs show the as-sprayed coating is dense with a uniform thickness and there are no coarse splat boundaries. The as-sprayed coating was chemically treated in 5 M NaOH solution at 80 degrees C for 48 h. The bioactivity of as-sprayed and alkaline-treated coatings was investigated by immersing the coatings in simulated body fluid (SBF) for 14-28 days, respectively. After 28 days immersion, there is a complete layer of carbon ate-containing apatite formed on the alkaline-treated TiO2 coating surface, but none formed on the as-sprayed coating. Published by Elsevier Ltd. on behalf of Acta Materialia Inc.