Imine-Linked Polymer-Derived Nitrogen-Doped Microporous Carbons with Excellent CO2 Capture Properties

A series of nitrogen-doped microporous carbons (NCs) was successfully prepared by direct pyrolysis of high-surface-area microporous imine-linked polymer (ILP, 744 m(2)/g) which was formed using commercial starting materials based on the Schiff base condensation under catalyst-free conditions. These NCs have moderate specific surface areas of up to 366 m(2)/g pore volumes of 0.43 cm(3)/g, narrow micropore size distributions, and a high density of nitrogen functional groups (5.58-8.74%). The resulting NCs are highly suitable for CO2 capture adsorbents because of their microporous textural properties and large amount of Lewis basic sites. At 1 bar, NC-800 prepared by the pyrolysis of ILP at 800 degrees C showed the highest CO2 uptakes of 1.95 and 2.65 mmol/g at 25 and 0 degrees C, respectively. The calculated adsorption capacity for CO2 per m(2) (mu mol of CO2/m(2)) of NC-800 is 7.41 mu mol of CO2/m(2) at 1 bar and 25 degrees C, the highest ever reported for porous carbon adsorbents. The isosteric heats of CO2 adsorption (Q(st)) for these NCs are as high as 49 kJ/mol at low CO2 surface coverage, and still similar to 25 kJ/mol even at high CO2 uptake (2.0 mmol/g), respectively. Furthermore, these NCs also exhibit high stability, excellent adsorption selectivity for CO2 over N-2, and easy regeneration and reuse without any evident loss of CO2 adsorption capacity.