期刊
ACS APPLIED MATERIALS & INTERFACES
卷 5, 期 9, 页码 3847-3854出版社
AMER CHEMICAL SOC
DOI: 10.1021/am4005072
关键词
electrospinning; cellulose nanocrystals (CNCs); nanocomposites; modification; poly(lactic acid); scaffolds
资金
- Louisiana Board of Regents [LEQSF-EPS(2013)-PFUND-318]
- National Key Technology R&D Program of China [2012BAD32B01]
Electrospun fibrous bio-nanocomposite scaffolds reinforced with cellulose nanocrystals (CNCs) were fabricated by using maleic anhydride (MAH) grafted poly(lactic acid) (PLA) as matrix with improved interfacial adhesion between the two components. Morphological, thermal, mechanical, and in vitro degradation properties as well as basic cytocompatibility using human adult adipose derived mesenchymal stem cells (hASCs) of MAH grafted PLA/CNC (i.e., MPLA/CNC) scaffolds were characterized. Morphological investigation indicated that the diameter and polydispersity of electrospun MPLA/CNC nanofibers were reduced with the increased CNC content. The addition of CNCs improved both the thermal stability and mechanical properties of MPLA/CNC composites. The MPLA/CNC scaffolds at the 5 wt % CNC loading level showed not only superior tensile strength (more than 10 MPa), but also improved stability during in vitro degradation compared with the MPLA and PLA/CNC counterparts. Moreover, the fibrous MPLA/CNC composite scaffolds were non-toxic to hASCs and capable of supporting cell proliferation. This study demonstrates that fibrous MPLA/CNC bio-nanocomposite scaffolds are biodegradable, cytocompatible, and possess useful mechanical properties for bone tissue engineering.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据