期刊
ACS APPLIED MATERIALS & INTERFACES
卷 5, 期 14, 页码 6586-6590出版社
AMER CHEMICAL SOC
DOI: 10.1021/am401222p
关键词
PDMS/Kapton adhesion; high-performance package; surface free energy; contact-angle measurements; scratch test; flexible thermoelectric generator
The present work highlights the progress in the field of polymeric package reliability engineering for a flexible thermoelectric generator realized by thin-film technology on a Kapton substrate. The effects of different plasma treatments on the mechanical performance at the interface of a poly-(dimethylsiloxane) (PDMS)/Kapton assembly were investigated. To increase the package mechanical stability of the realized wearable power source, the Kapton surface wettability after plasma exposure was investigated by static contact-angle measurements using deionized water and PDMS as test liquids. In fact, the well-known weak adhesion between PDMS and Kapton can lead to a delamination of the package with an unrecoverable damage of the generator. The plasma effect on the adhesion performances was evaluated by the scratch-test method. The best result was obtained by performing a nitrogen plasma treatment at a radio-frequency power of 20 W and a gas flow of 20 sccm, with a measured critical load of 1.45 N, which is 2.6 times greater than the value measured on an untreated Kapton substrate and 1.9 times greater than the one measured using a commercial primer.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据