期刊
ACS APPLIED MATERIALS & INTERFACES
卷 3, 期 3, 页码 765-773出版社
AMER CHEMICAL SOC
DOI: 10.1021/am101125d
关键词
high temperature polyimide; anthracene moiety; nanoscale thin film; amorphous; in-plane orientation; nonvolatile polymer memory; bipolar switching; unipolar switching; space-charge-limited current; local filament formation
资金
- National Research Foundation (NRF) of Korea of the Ministry of Education, Science and Technology (MEST)
- POS-CO
- POSTECH Foundation
A high temperature polyimide bearing anthracene moieties, poly(3,3'-di(9-anthracenemethoxy)-4,4'-biphenylene hexafluoroisopropylidenediphthalimide) (6F-HAB-AM PI) was synthesized. The polymer exhibits excellent thermal stability up to around 410 degrees C. This polymer is amorphous but orients preferentially in the plane of nanoscale thin films. In device fabrications of its nanoscale thin films with metal top and bottom electrodes no diffusion of the metal atoms or ions between the polymer and electrodes was found; however, the aluminum bottom electrode had somewhat undergone oxide layer (about 1.2 nm thick) formation at the surface during the post polymer layer formation process, which was confirmed to have no significant influence on the device performance. The polymer thin film exhibited excellent unipolar and bipolar switching behaviors over a very small voltage range, less than +/- 2 V. Further, the PI films show repeatable writing, reading, and erasing ability with long reliability and high ON/OFF current ratio (up to 10(7)) in air ambient conditions as well as even at temperatures up to 200 degrees C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据