Easy Route to the Wettability Cycling of Copper Surface between Superhydrophobicity and Superhydrophilicity

期刊

ACS APPLIED MATERIALS & INTERFACES
卷 4, 期 1, 页码 273-279

出版社

AMER CHEMICAL SOC
DOI: 10.1021/am2013129

关键词

materials science; surface chemistry; CuO; wettability cycling; desorption

向作者/读者索取更多资源

A hierarchical copper structure combining micro- and nanogaps/pores was built up on copper substrate by etching and electrodeposition. The fresh as-deposited copper was easily oxidized in air at room temperature, forming a CuO layer covering on the surface. The surface could be hydrophobized with thiol-modified fluorocarbons, after which it showed a water contact angle as high as 165 degrees +/- 2 degrees. This surface could also regain the superhydrophilicity with a zero water contact angel after annealing at 200 degrees C for 10 min to desorb the low surface energy monolayer of thiol-modified fluorocarbons and reform a CuO layer again on the surface. Repeating the process of adsorption/desorption of the monolayer by modification and annealing, it was successful to fulfill the wettability cycling between superhydrophobicity and superhydrophilicity on the copper surface. The adsorption and desorption mechanism of the monolayer was discussed based on the result of surface chemistry analysis.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.8
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据