The effect of a nanoscale boron subphthalocyanine chloride (SubPc) interfacial layer on the performance of inverted polymer solar cells based on poly (3-hexyl thiophene) (P3HT) and [6,6]-phenyl-C-71-butyric acid methyl ester (PC71BM) was studied. When a 1 nm SubPc layer was introduced between the active layer (P3HT:PC71BM) and MoOx, in the device with ITO/ZnO/P3HT:PC71BM/SubPc/MoOx/Al configuration, the power conversion efficiency (PCE) was increased from 3.42 (without SubPc) to 3.59%. This improvement is mainly attributed to the enhanced open-circuit voltage from 0.62 to 0.64 V. When the Flory-Huggins interaction parameters were estimated from the solubility parameters through the contact angle measurement, it revealed that the interaction between SubPc and PC71BM is more attractive than that between SubPc and P3HT at the interface of P3HT:PC71BM/SubPc, through which charges are well transported from the active layer to the anode. This is supported by a decrease of the contact resistance from 5.49 (SubPc 0 nm) to 0.94 M Omega cm (SubPc 1 nm). The photoelectron spectra provide another evidence for the enhanced PCE, exhibiting that the 1 nm thick SubPc layer extracts more photoelectrons from the active layer than other thicknesses.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据