polymer solar cells; degradation; failure mechanism; TOF-SIMS; P3HT; MEH-PPV
资金
- Danish Strategic Research Council (DSF) [2104-04-0030, 210405-0052, 2104-07-0022]
Water-induced degradation of polymer photovoltaics based on the active materials poly(3-hexylthiophene) (P3HT) or poly[2-methoxy-5-(2'-ethylhexyloxy)-1,4-phenylenevinylene] (MEHPPV) was studied. The solar cell devices comprised a bulk heterojunction formed by the active material and [6,6]-phenyl-C-61-butyric acid methyl ester (PCBM) in a standard device geometry. The use of (H2O)-O-18 in conjunction with time-of-flight secondary ion mass spectrometry enabled mapping of the parts of the device that were induced by water. A comparison was made between the two active materials and between devices that were kept in the dark and devices that had been subjected to illumination under simulated sunlight. Devices that were exposed to ambient humidity were compared to devices exposed to saturated humidity. Finally, a comparison was made between results obtained using (H2O)-O-18 and earlier work involving O-18(2). Water was found to have behavior similar to but not identical with molecular oxygen.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据