期刊
ACS ENERGY LETTERS
卷 3, 期 3, 页码 568-+出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsenergylett.7b01321
关键词
-
类别
资金
- Department of Energy, Office of Energy Efficiency and Renewable Energy (EERE) [DE-EE0007218]
Sulfur cathodes have a high theoretical capacity of 1675 mAh g(-1), making the lithium-sulfur batteries a promising technology for future energy-storage devices. However, their commercial viability is faced with challenges arising from intrinsic electrochemical instabilities and inappropriate cell fabrication parameters. We report here the feasibility of employing TiS2 as a conductive polysulfide adsorbent, which allows the use of a high amount of electrochemically active polysulfides in building a TiS2-polysulfide hybrid cathode. The hybrid cathode exhibits long cycle stability at a C/5 rate over 200 cycles with a high areal capacity and energy density of, respectively, 10 mAh cm(-2) and 20 mWh cm(-2), exceeding those of commercial LiCoO2. Such an enhanced electrochemical performance is obtained in cells with a high sulfur content (65 wt %), high sulfur loading (12 mg cm(-2)), high sulfur mass (12 mg/cathode), and a low electrolyte/sulfur ratio of just 5 mu L mg(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据