期刊
COATINGS
卷 8, 期 5, 页码 -出版社
MDPI
DOI: 10.3390/coatings8050195
关键词
thermal barrier coating (TBC); high-temperature exposure; thermally grown oxide (TGO); Cr oxide; oxidation kinetics
资金
- Harbin Engineering University
- National Technology Foundation of China [JSZL 2014601B004, JSZL 2017601C002]
Thermal barrier coating (TBC) is a critical material in the aerospace domain to increase the lifetime of gas turbine components subjected to thermal load. The properties of TBC are strongly related to the growth of thermally grown oxide (TGO) whose main constituent is Al2O3. However, the oxidation of Cr and Co can affect the growth of TGO, which is not studied sufficiently. In this paper, high-temperature exposure at 1000 degrees C was performed to investigate the effect of Cr and Co oxides on TGO growth. The morphology and composition analysis of the interface between the ceramic top coat and the bond coat (TC/BC) were investigated by using scanning electron microscopy (SEM) and the energy dispersion spectrum (EDS). The thermodynamics and kinetics of oxidation were analyzed. The results indicated that the oxidation kinetics basically followed the sub-parabolic law with exposure time. Additionally, the major factor affecting the formation of oxides was the diffusion rate at the initial stage of exposure, then oxides depended on thermodynamics, and the oxidation was influenced by both of them in the last stage. The major elements to be oxidized were different at different stages. Moreover, the replacement reaction of Cr2O3 and the phase conversion of Al2O3 resulted in thickness variations of the TGO and Al-depleted zone during high-temperature exposure.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据