Transition Metal Ion (Mn2+, Fe2+, Co2+, and Ni2+)-Doped Carbon Dots Synthesized via Microwave-Assisted Pyrolysis: A Potential Nanoprobe for Magneto-fluorescent Dual-Modality Bioimaging

Heteroatom-doped carbon dots (C-dots) have captured widespread research interest owing to high fluorescence and biocompatibility for multimodal bioimaging applications. Here, we exemplify a rapid, facile synthesis of ethylenediamine (EDA)-functionalized transition metal ion (Mn2+, Fe2+, Co2+, and Ni2+)-doped C-dots via one-pot microwave (MW)-assisted pyrolysis at 800 W within 6 min using Citrus limon (lemon) extract as a carbon source. During MW pyrolysis, the precursor extract undergoes simultaneous carbonization and doping of metal ions onto C-dot surfaces in the presence of EDA. The EDA-functionalized transition metal ion-doped C-dots (i.e., Mn/C, Fe/C, Co/C, and Ni/C-dots) are collectively termed as TMCDs. The water-soluble TMCDs exhibited a size of 3.2 +/- 0.485 nm and were enriched with amino and oxo functionalities and corresponding metal-oxide traces on the surfaces, as revealed from Fourier transfer infrared and X-ray photoelectron spectroscopy analyses. Interestingly, TMCDs demonstrated excitation-wavelength-dependent emission with brighter photoluminescence (PL) at 460 nm. Compared to pristine C-dots with a PL quantum yield (QY) of 48.31% and a fluorescence lifetime of 3.6 ns, the synthesized Mn/C, Fe/C, Co/C, and Ni/C-dots exhibited PL QY values of 35.71, 41.72, 75.07, and 50.84% as well as enhanced fluorescence lifetimes (tau(av)) of 9.4, 8.6, 9.2, and 8.9 ns, respectively. The TMCDs significantly exhibited enhanced biocompatibility in human colon cancer cells (SW480) for fluorescence bioimaging and showed ferromagnetic and superparamagnetic behavior with vibrant T-1-contrast ability. Interestingly, the maximum longitudinal (r(1)) relaxivity of 0.341 mM(-1) s(-1) was observed for Mn/C-dots in comparison to that of 3.1-3.5 mM(-1) s(-1) of clinically used Gd-DTPA magnetic resonance (MR)-contrast agent in vitro (1.5 T). Similarly, the maximum longitudinal relaxivity (r(1)) of 0.356 mM(-1) s(-1) was observed for Ni/C-dots (1.5 T) with respect to 4.16 +/- 0.02 mM(-1) s(-1) attained for Gd-DTPA in vivo (8.45 T). Thus, the rapid, energy-efficient MW-assisted pyrolysis presents lemon extract derived, EDA-functionalized TMCDs with enhanced PL and efficient T-1 contrast as potential magneto-fluorescent nanoprobes for dual-modality bioimaging applications.