期刊
MATERIALS & DESIGN
卷 142, 期 -, 页码 124-137出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2018.01.007
关键词
Dilution rate; FexCoCrNi; FCC crystal lattice; Lattice dislocation; Self-passivation ability; High-temperature oxidation
资金
- National Nature Science Foundation of China [51275342, 51405334, 51405335]
The influence of laser parameters and alloying elements on the dilution rate of FeCoCrNi coating was investigated. It was found that the alloying elements have more significant effect on the dilution rate than the laser cladding parameters. Optical microscopy, scanning electron microscopy, X-ray diffraction analysis, micro-hardness test, wear test, electrochemical corrosion test, and high-temperature oxidation test were conducted to study the influence of dilution rate on the microstructure and properties of the FexCoCrNi coatings. The results have shown that the transfer of Fe element from the substrate could make the mixed entropy of the Fe0CoCrNi coating close to the theoretical mixed entropy of the FeCoCrNi high-entropy alloy. Excess Fe element in the original powder increased the dilution rate, leading to a reduction in the mixed entropy of the coating. However, it did not lead to the generation of new phases in the coating. The atomic radius differences between the elements could lead to large lattice distortion in the FCC crystal lattice. The level of lattice distortion and micro-hardness of the FexCoCrNi coatings increased with increasing Fe element content. Furthermore, the excess Fe elements weakened the self-passivation ability and deteriorated the high-temperature oxidation resistance of the coating. (c) 2018 Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据