期刊
ADVANCED MATERIALS INTERFACES
卷 5, 期 14, 页码 -出版社
WILEY
DOI: 10.1002/admi.201800331
关键词
colloidal synthesis; morphological stability; photothermal effect; pollutant degradation; trimetallic plasmonic nanohybrids
资金
- National Research Foundation of Korea [NRF-2016R1D1A1B03934226, 2016R1A2A2A07005160]
Herein, preparation of novel multimetallic core-satellite Pt-nanodots decorated TiO2-coated AuNPs (AuNPs@TiO2@Pt) plasmonic nanoparticles with well-defined spherical dendritic morphology and excellent colloidal stability are reported. The coating of a TiO2 layer and PtNDs maximizes the surface plasmon resonance as there is a redshift from 525 to 550 nm and also increases surface area significantly. Prepared plasmonic nanohybrid is tested for multiple photosystems such as water pollutants (methylene blue, methyl orange, and methyl red) photodegradation at room temperature in visible light irradiation, and photothermal studies in near-infrared (NIR, 808 nm) light. AuNPs@TiO2@Pt shows complete photocatalytic degradation of organic dyes (methylene blue = 40 min, methyl orange = 75 min, and methyl red = 60 min) at room temperature and the pseudo first-order rate constant is found to be 0.1242, 0.047, and 0.068 min(-1) for methylene blue, methyl orange, and methyl red degradation, respectively. Moreover, AuNPs@TiO2@Pt also shows a high photothermal effect in NIR light irradiation with an excellent morphological and photostability.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据