期刊
JOURNAL OF MATERIALS CHEMISTRY B
卷 6, 期 11, 页码 1613-1621出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c8tb00088c
关键词
-
资金
- Ministry of Science and Higher Education [7150/E-338/M/2017]
- European Regional Development Fund [POIG.02.01.00-12-023/08]
- European Regional Development Found Operational Program Infrastructure and Environment [POIS 13.01.00-00-062/08]
- Malopolska Regional Operational Program Measure 5.1 Krakow Metropolitan Area as an important hub of the European Research Area [MRPO.05.01.00-12-013/15]
Poly(n-butyl methacrylate) (PBMA) grafted polymer brushes attached to glass were fabricated in a three-step process involving surface initiated atom transfer radical polymerization. The surface properties of the coatings after subsequent fabrication steps were confirmed using ToF-SIMS and ellipsometry. Measurements of water contact angle and AFM revealed temperature-induced changes in the hydrophobicity and morphology of the coating. The glass transition temperatures (T-g) of the PBMA coatings with different thicknesses were determined from the AFM measurements. For the PBMA grafted brush coatings with thicknesses less than 62 nm, T-g increases sharply with increasing thickness. The PBMA grafted coatings of thickness equal to 86 nm and 43 nm as well as control glass substrates were used as substrates for culturing a urinary bladder cancer HTB-5 cell line. After 144 h of culturing, a well-developed monocellular layer may be observed on the PBMA coating of thickness equal to 86 nm. In turn, the cells incubated on thinner (43 nm) PBMA coatings as well as on a control glass sample only start to form a confluent layer.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据