IEEE TRANSACTIONS ON MAGNETICS
卷 51, 期 6, 页码 -出版社
IEEE-INST ELECTRICAL ELECTRONICS ENGINEERS INC
DOI: 10.1109/TMAG.2014.2381155
关键词
Grain size (GS); non-oriented silicon steel; texture
Industrial rough bar samples of 2% Si were hot rolled in a pilot reversing mill at different finishing temperatures. Hot rolled bands 2.3 mm in thickness were cold rolled to 0.50 mm and final annealed at different temperatures under H-2-N-2 atmosphere. To study the effect of hot band annealing, some samples were annealed at 1030 degrees C before cold rolling. Crystallographic texture and grain size (GS) were measured at the different processing steps. Magnetic properties were measured after final annealing. The results have shown that in case of finishing reversible hot rolling, hot band annealing may not result in benefit for magnetic properties due to the effect of static recrystallization between passes that already generates coarse hot band structure. Hot band GS has strong effect on final structure and magnetic properties. The increase of hot band GS has a beneficial effect on texture and magnetic polarization J(50) due to the increase of eta fiber fraction. However, large initial GS may result in smaller GS after final annealing due to intensive nucleation in shear bands on recrystallization. On further grain growth, the fraction of eta fiber grains tend to decrease, resulting in simultaneous decrease of J(50) and core loss.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据