Fiber-reinforced polymer; Laminates; Cross-ply; Unidirectional; Impact strength
The impact behavior of glass fibers reinforced polyester (GFRP) was experimentally investigated using notched Izod impact test specimen. The experimental program was carried out on unidirectional laminate of GFRP in directions 0 degrees, 45 degrees and 90 degrees in addition to cross-ply laminate (0/90/(0) over bar)(s). The effect of fiber volume fraction, V-f% (16%, 23.2% and 34.9%) was considered. The impact specimens were tested after exposure to temperatures of -10 degrees C, 20 degrees C, 50 degrees C and 80 degrees C for exposure time of 1 h and 3 h. Test results showed that the effect of exposure temperature and fiber volume fraction on impact strength of GFRP composite depends on the parameter controlling the mode of failure, i. e. matrix or fiber. The failure characteristic changed from fiber pull-out to fiber breakage with increasing the exposure temperature. (C) 2012 Ain Shams University. Production and hosting by Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据