OPTICAL MATERIALS EXPRESS
卷 8, 期 7, 页码 1841-1849出版社
OPTICAL SOC AMER
DOI: 10.1364/OME.8.001841
关键词
-
资金
- National Natural Science Foundation of China [51602117]
To explore new upconversion materials for optical temperature sensing, a series of Tm3+-Yb3+ codoped Y4.67Si3O13 (YSO) phosphors was prepared by solid-state reaction. The phase composition was examined by XRD patterns, revealing that the samples are single-phase. Upon 980 nm excitation, four main emission peaks of Tm3+ were observed from the near-ultraviolet to the near-infrared region. The pump-dependence measurement indicates that the blue and near-infrared emissions of Tm3+ are three- and two-photon processes, respectively. By studying the temperature-dependence of the typical YSO:0.5%Tm3+, 10%Yb3+ sample, it has been found that the fluorescence intensity ratios (FIRs) of both the 695/789 and 466/484 nm emissions increase with increasing temperature due to the thermally-coupled levels. The repeatability of measurement was examined by relative standard deviation and cycle test. The relative and absolute sensitivities of YSO:0.5%Tm3+, 10%Yb3+ were evaluated. (C) 2018 Optical Society of America under the terms of the OSA Open Access Publishing Agreement
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据