SA508-IV steel; Hot deformation; Processing map; Microstructural evolution
资金
- Beijing Municipal Natural Science Foundation [2162026]
- 863 Program of China [2008AA031702, 2012AA03A507]
The hot deformation behavior and microstructural evolution of SA508-IV steel for a novel nuclear reactor pressure vessels were studied by hot compression tests in the strain rates 0.001-1 s(-1) and temperature ranges 950-1250 degrees C respectively. The results showed that the high temperature (1250 degrees C) and low strain rate (0.001 s(-1)) were more likely to induce the abnormal growth of grains, resulting in the decrease of the power dissipation efficiency. The flow instability region covered the temperature and strain rate ranges in 950-1200 degrees C and 0.1-1 s(-1) with inhomogeneous microstructure. The optimal processing window of SA508-IV steel was obtained in the temperature ranges 1050-1175 degrees C and strain rates 0.01-0.1 s(-1) respectively with a peak efficiency of 45%. By analyzing the microstructure of the steel in this zone mentioned above, fine recrystallized grains were got.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据