W-Cu composites; Sintering; Infiltration; Microstructure; Arc erosion
资金
- 863 Program [2015AA034304]
- National Natural Science Foundation of China [51604223, 51371139]
- Science and Technology Project of Shaanxi Province [2016JQ5025]
- Key Laboratory Foundation of Shaanxi Provincial Department of Education [16JS064]
In the present work, characteristics regarding the sub-micron scale microstructure of the W-30 wt%Cu contact material after vacuum electrical breakdown have been investigated by SEM and EDS. EBSD was also utilized to reveal the change of grain size, misorientation and micro-texture for both Cu and W phases after arc erosion. The results revealed that the arc erosion led to distinct grain refinement and intensified local misorientation strain. Besides, with the help of orientation distribution function analysis, strong peak type {112}< 4-61 > component was identified to be an important arc erosion texture for the first breakdown phase of Cu, which would complicate the following breakdown process during service due to the work function anisotropies. (C) 2018 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据