期刊
TRIBOLOGY INTERNATIONAL
卷 126, 期 -, 页码 344-351出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.triboint.2018.05.033
关键词
Nanostructured Ti/Al multilayers; Plasticity; Fracture; Work of adhesion
资金
- Faculty Research Cluster Program, the University of Sydney
- Australian Microscopy and Microanalysis Research Facility node at the University of Sydney
This paper presented a comparative study on plasticity and fracture behaviour of nanostructured Ti/Al multilayers with two individual layer thicknesses X. The nanoindentation results showed that film buckling appears in the 10 nm multilayer, whereas localised shear bands are detected in the 100 nm multilayer. The nanoscratch results indicated that localised conformal cracks and spalling are the dominant fracture mode in the multilayer with lambda = 10 nm, whereas adhesive failure is observed in the 100 nm multilayer when a critical normal load is reached. The work of adhesion of the 10 nm multilayer was much larger than that with lambda = 10 nm, possibly due to the high hardness and few dislocation slips by the confined layer mechanism.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据