期刊
SURFACE & COATINGS TECHNOLOGY
卷 349, 期 -, 页码 529-539出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2018.06.030
关键词
Multiprincipal element nitride; High-entropy nitride; Two-phase nitride; Transition metal nitride; Tetragonal distortion; Thin films
资金
- Swedish Research Council via VR-RFI [C0514401]
- Swedish Foundation for Strategic Research via SSF [RIF14-0053]
Multicomponent nitride coatings of the Hf-Nb-Ti-V-Zr system with different Hf content (0-18 at.%) were deposited using reactive dc magnetron sputtering. Coatings with lower Hf content (0-7 at.%) were found to consist of a single solid solution phase with NaCl-type structure (space group Fm-3m). Coatings with higher Hf content (10-18 at.%) showed a two-phase material consisting of cubic Fm-3m and tetragonal I4/m:run solid solution phase. The lattice distortion, estimated by calculating the delta-parameter under the assumption of a single solid solution phase, varied between 3.8 and 4.0% and slightly decreased with increasing Hf content. SEM and TEM cross section images showed a columnar microstructure with columns that were frayed on the surface or throughout the whole column. The column size decreased as Hf content increased. The hardness increased from 8 to 19 GPa with increased Hf content, which most probably is related to the change in microstructure rather than change in lattice distortion. The electrical resistivity for all samples ranged between 231 and 286 mu Omega cm.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据