期刊
RUSSIAN JOURNAL OF PHYSICAL CHEMISTRY A
卷 92, 期 3, 页码 430-437出版社
MAIK NAUKA/INTERPERIODICA/SPRINGER
DOI: 10.1134/S0036024418030147
关键词
methane; oxidative coupling; oxide catalysts; lattice oxygen
资金
- Russian Foundation for Basic Research [16-33-50273 mol_nr]
- Boreskov Institute of Catalysis, Russian Academy of Sciences [0303-2016-0013]
- RF Ministry of Education and Science
Mixed NaWMn/SiO2 oxide, samples containing individual components (Na, W, Mn) and their double combinations (Na-W, Na-Mn, W-Mn) supported on silica were studied by temperature programmed reduction (TPR) and desorption (TPD), and heat flow calorimetry during their reoxidation with molecular oxygen in pulse mode. The NaWMn/SiO2 mixed oxide was shown to contain two different types of reactive lattice oxygen. The weakly-bonded oxygen can be reversibly released from the oxide in a flow of inert gas in the temperature range of 575aEuro'900A degrees C, while the strongly-bonded oxygen can be removed during the reduction of the sample with hydrogen at 700-900A degrees C. The measured thermal effect of oxygen consumption for these two oxygen forms are 185 and 350 kJ/mol, respectively. The amount of oxygen removed at reduction (similar to 443 mu mol/g) considerably exceeded the amount desorbed in an inert gas flow (similar to 56 mu mol/g). The obtained results suggest that the reversible oxygen desorption is due to the redox process in which manganese ions are involved, while during the temperature programmed reduction, mainly oxygen bonded with tungsten is removed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据